Electrical resistivity of bulk multi-walled carbon nanotubes synthesized by an infusion chemical vapor deposition method
Multi-walled carbon nanotubes (MWNTs) were synthesized by infusing alcohol into a tube furnace. A nickel catalyst preparation was made by a reduction reaction of NiO powder by ethanol vapor at 450 °C for 30 min before the MWNT synthesis at 700 °C for 1-18 h. The as-grown MWNTs were characterized by...
محفوظ في:
| المؤلفون الرئيسيون: | , , |
|---|---|
| التنسيق: | دورية |
| منشور في: |
2018
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=33751105038&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/61092 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | Multi-walled carbon nanotubes (MWNTs) were synthesized by infusing alcohol into a tube furnace. A nickel catalyst preparation was made by a reduction reaction of NiO powder by ethanol vapor at 450 °C for 30 min before the MWNT synthesis at 700 °C for 1-18 h. The as-grown MWNTs were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction and Raman spectroscopy. Large quantities of MWNTs, having a diameter in the range of 20-50 nm can be produced from ethanol vapor without a carrier gas by this technique. A method to measure an electrical resistance of bulk MWNTs was carried out under stress between two conducting plates. The result shows an exponentially correlation between the resistivity and the D-band/G-band intensity ratio, suggesting that the measuring method provides a simple tool to monitor the degree of structural defects of MWNTs. © 2006 Elsevier B.V. All rights reserved. |
|---|