Mechanical characterization and analysis of thin-film stacked structures for microelectronic assembly

• Main Author: Yeo, Swain Hong
• Other Authors: Zhou Kun
• Format: Theses and Dissertations
• Language: English
• Published: 2017
• Subjects: DRNTU::Engineering::Materials::Microelectronics and semiconductor materials::Thin films; DRNTU::Engineering::Materials::Material testing and characterization; DRNTU::Engineering::Electrical and electronic engineering::Electronic packaging
• Online Access: http://hdl.handle.net/10356/72665
• Institution: Nanyang Technological University

The trend towards cost reduction, improved reliability, and increased functionality and performance in the power electronic product leads to a continuous implementation of new designs, materials, processes, and evaluation methodologies for chip- and package-level interconnections. Due to such trend, the shrinking of integrated circuit (IC) features has raised a serious concern about the robustness of the thin-film stacked structure in the bond pad of an IC chip, especially on the wafer probe testing and wire bonding process in the chip-to-package interconnection. Furthermore, copper (Cu) wires have started to replace gold (Au) wires in the wire interconnection due to their superb cost advantageous, and excellent thermal and electrical performances. However, this hard Cu material makes the wire bonding on the bond pad of an IC chip much more challenging, where excessive deformation and damage of sensitive structures underneath the bond pad could happen. Moreover, cracking normally occurs at a brittle hard dielectric layer underneath the top metallization pad, which is not visible and difficult to detect, and thus it is important to understand and predict the mechanical response of the thin-film stacked structure of the bond pad under the wire bonding process. Hence, this research aims to study the mechanical behaviors and damage mechanisms of the thin-film stacked structures under indentation loading through both experimental study and numerical simulation. Firstly, an indentation damage test method is established using a micro-mechanical tester integrated with an acoustic emission (AE) sensor for crack detection in the specimen during the indentation loading-unloading cycle. The bulk Si die is first employed to investigate the integration of the indentation testing with the AE sensing, where the AE signal response is examined upon the occurrence of the onset cracking at the critical force Fc or displacement dc. The effects of the coupling medium between the specimen and AE sensor, and the specimen indentation position on the AE signal response are systematically studied. Secondly, the indentation damage test is employed to evaluate the bulk Si die and different thin-film stacked systems consisting of a top metal layer (aluminium Al or copper-titanium CuTi) and intermediate dielectric (silicon dioxide SiO2 or silicon nitride Si3N4) layers on the Si substrate. During the indentation, the first AE event corresponds to the “pop-in” or plateau is observed in the F-d curve, which is mainly due to the brittle cracking in the dielectric layer or/and Si substrate. Different failure modes are observed for different dielectric layers used in the thin-film stacked system, independent of the top metal layer materials. Besides the first AE event, a second or more AE events are also detected during the unloading stage due to the elastic recovery of the specimen, which lead to further crack propagation and delamination within the thin-film layers. A finite element model is established to simulate the loading-unloading process of the indentation on the bulk Si and the thin-film stacked system. The stress analysis is performed and correlated to the cracking of the specimens subjected to the indentation test, in which the damage mechanisms are uncovered. Thirdly, the work of indentation damage and fracture on the specimen are investigated. An indentation energy-based approach is proposed to determine the work of indentation fracture Wf based on the difference in elastic strain recovery between a damaged and a non-damaged specimen from the same maximum force, where the unloading begins. Two different techniques are developed to estimate Wf, namely the elastic-to-total work ratio and the integration of the unloading F-d curve. The relationship of the calculated Wf and the measured EAE is analyzed and discussed. In summary, this PhD study contributes to the understanding of the deformation, damage and cracking behavior of the thin-film stacked system subjected to the indentation loading-unloading cycle. This is essential in the processes of the wafer probing and wire bonding on the bond pad of an IC device, where the damage-sensitive pad can be identified and handled with care. Furthermore, the methodology can be used to optimize the structural robustness of the bond pad design, or implement as a mechanical screening tool for wafer quality check, which provides guidance in achieving optimal design for manufacturing reliable and durable microelectronic devices.